SLA Resin Standard

SLA Resin Standard (Formlabs Clear V5) strength, stiffness, density and thermal properties, with their source.

A bracket in SLA Resin Standard, smooth finish.

Mechanical
Process	3D printed (SLA resin)
Yield strength	not given (tensile used)
Ultimate tensile strength	60MPasourcetypical
Flexural strength	105MPasourcetypical
Elongation at break	8%sourcetypical
Young's modulus (stiffness)	2.75GPasourcetypical
Density	not sourced
Strength to weight	not sourced
Stiffness to weight	not sourced
Poisson's ratio	not sourced
Shear modulus	not sourced
Bulk modulus	not sourced
Speed of sound	not sourced
Thermal
Thermal conductivity	not sourced
Thermal expansion	not sourced
100 mm part over a 50 °C swing	not sourced
Specific heat	not sourced
Heats up and cools (diffusivity)	not sourced
Thermal shock resistance	not sourced
Max service temperature	59°CsourceHDT 1.8 MPa
Values for	Formlabs Clear Resin V5 (FLGPCL05), TDS Rev. 01 March 20, 2024; printed on Form 4 at 100 µm, washed 5 min in >=99% IPA, post-cured 15 min at 60 °C in Form Cure. Orientation not stated.

SLA Resin Standard is 3D printed: its properties depend on build direction and print settings; these are typical values.

Among 59 materials

Stiffness against density

Strength against density