Materials / Compare
Copper C110 vs. Wood Compare Copper C110 vs. Wood strength, stiffness, weight and thermal properties.
Change either side
Plastic PLA Plastic PETG Plastic ABS Plastic TPU Plastic Nylon Plastic ABS (bulk/injection) Plastic Polycarbonate Plastic POM/Acetal Plastic Nylon PA6 Plastic Nylon PA66 Plastic PEEK Plastic PTFE Plastic UHMWPE Plastic HDPE Plastic Polypropylene Plastic PMMA Rubber Wood Aluminum Aluminum 6061-T6 Aluminum 7075-T6 Aluminum 2024-T351 Aluminum 5052-H32 Aluminum 7050-T7451 Steel Steel AISI 1018 Steel AISI 1045 Steel AISI 4340 Steel A992 Iron Titanium Titanium Ti-6Al-4V Stainless 304 Stainless 316 Stainless 303 Stainless 17-4PH Brass C360 Brass C260 Copper C110 Glass Nickel Inconel 718 Magnesium AZ31B-H24 Zinc Zamak 3 FDM ASA FDM Polycarbonate FDM PAHT-CF FDM HIPS SLA Resin Standard SLA Resin Tough 2000 SLA Resin Elastic 50A SLS PA12 Nylon DMLS AlSi10Mg Aluminum DMLS Ti-6Al-4V ELI Titanium DMLS 316L Stainless Steel DMLS 17-4PH Stainless Steel Concrete Brick Plywood Drywall Copper C110 Wrought Plastic PLA Plastic PETG Plastic ABS Plastic TPU Plastic Nylon Plastic ABS (bulk/injection) Plastic Polycarbonate Plastic POM/Acetal Plastic Nylon PA6 Plastic Nylon PA66 Plastic PEEK Plastic PTFE Plastic UHMWPE Plastic HDPE Plastic Polypropylene Plastic PMMA Rubber Wood Aluminum Aluminum 6061-T6 Aluminum 7075-T6 Aluminum 2024-T351 Aluminum 5052-H32 Aluminum 7050-T7451 Steel Steel AISI 1018 Steel AISI 1045 Steel AISI 4340 Steel A992 Iron Titanium Titanium Ti-6Al-4V Stainless 304 Stainless 316 Stainless 303 Stainless 17-4PH Brass C360 Brass C260 Copper C110 Glass Nickel Inconel 718 Magnesium AZ31B-H24 Zinc Zamak 3 FDM ASA FDM Polycarbonate FDM PAHT-CF FDM HIPS SLA Resin Standard SLA Resin Tough 2000 SLA Resin Elastic 50A SLS PA12 Nylon DMLS AlSi10Mg Aluminum DMLS Ti-6Al-4V ELI Titanium DMLS 316L Stainless Steel DMLS 17-4PH Stainless Steel Concrete Brick Plywood Drywall Wood Natural Try it on a partA bracket to run stress or thermal on, free in your browser Open in LessCAD Open in LessCAD Mechanical Yield strength 69 MPa source typical, 0.5% extension under load not given (tensile used) Ultimate tensile strength 221 MPa source typical 99 MPa source modulus of rupture (no direct tensile value) Compressive strength not sourced 46.6 MPa source compression parallel to grain (maximum crushing strength), 12% MC Flexural strength not sourced 99 MPa source modulus of rupture (static bending), 12% MC Elongation at break 55 % source typical, 1 in. rod not sourced Young's modulus (stiffness) 117 GPa source typical 12.5 GPa source bending MOE, parallel to grain Density 8,913 kg/m³ source nominal not sourced Strength to weight 7.74 kN·m/kg not sourced Stiffness to weight 13.1 MN·m/kg not sourced Poisson's ratio 0.34 source reference value at room temperature (Wieland-K32 = Cu-ETP = C11000, rolled products) 0.35 source mu_LR (red oak group, ~12% MC) Shear modulus 43.7 GPa 9.45x stiffer in shear 4.63 GPa Bulk modulus 122 GPa 13.9 GPa Speed of sound 3,626 m/s not sourced Thermal Thermal conductivity 391 W/m·K source typical, 20 °C 0.18 W/m·K source across grain, 12% MC (Table 4-7, approximate) Thermal expansion 16.9 µm/m·K source typical, mean 20-100 °C 3.1–4.5 µm/m·K source parallel to grain, ovendry wood, range across species 100 mm part over a 50 °C swing 84.5 µm growth 19 µm growth 4.45x less Specific heat 385 J/kg·K source typical, 20 °C 1,700 J/kg·K source solid wood (all species), 12% MC, 27 C Heats up and cools (diffusivity) 114 mm²/s not sourced Thermal shock resistance 8,992 W/m 36.9x more resistant 244 W/m Melting point 1,065–1,083 °C source solidus-liquidus not sourced Values for C11000 ETP copper, annealed to 0.050 mm grain size (OS050), 1 in. rod, copper.org typical values Northern red oak (Quercus rubra), clear straight-grained specimens at 12% MC, parallel to grain unless stated; USDA FPL Wood Handbook FPL-GTR-282 (2021) Ch. 4 and Ch. 5
Every value links to the document that states it. "Not sourced" means no citable source states it (or only a specification minimum); figures computed from it are left out too.
Questions Is Copper C110 stronger than Wood? Wood is stronger: its tensile strength is 99 MPa against yield strength 69 MPa for Copper C110 (43%).
Which is stiffer, Copper C110 or Wood? Copper C110 is stiffer: Young's modulus 117 GPa against 12.5 GPa for Wood, so the same part in Copper C110 deflects less under the same load.
Which conducts heat better, Copper C110 or Wood? Copper C110 conducts heat better: 391 W/m·K against 0.18 W/m·K for Wood.
Which expands less with temperature? Wood expands less: 3.8 µm/m·K against 16.9 µm/m·K for Copper C110.
Among 59 materials 1k 10k 0.1 1 10 100 Density (kg/m³) Young's modulus (GPa) Plastic PLA Plastic PETG Plastic ABS Plastic TPU Plastic Nylon Aluminum Steel Iron Titanium Steel AISI 1018 Stainless 304 Stainless 316 Aluminum 6061-T6 Aluminum 7075-T6 Brass C360 Glass Steel AISI 1045 Steel AISI 4340 Steel A992 Stainless 303 Stainless 17-4PH Aluminum 2024-T351 Aluminum 5052-H32 Aluminum 7050-T7451 Titanium Ti-6Al-4V Brass C260 Nickel Inconel 718 Magnesium AZ31B-H24 Zinc Zamak 3 Plastic ABS (bulk/injection) Plastic Polycarbonate Plastic POM/Acetal Plastic Nylon PA6 Plastic Nylon PA66 Plastic PEEK Plastic UHMWPE Plastic HDPE Plastic Polypropylene Plastic PMMA FDM ASA FDM Polycarbonate FDM PAHT-CF FDM HIPS SLA Resin Tough 2000 SLS PA12 Nylon DMLS AlSi10Mg Aluminum DMLS Ti-6Al-4V ELI Titanium DMLS 316L Stainless Steel DMLS 17-4PH Stainless Steel Copper C110 Stiffness against density 1k 10k 10 100 1k Density (kg/m³) Yield strength (MPa) Plastic PLA Plastic PETG Plastic ABS Plastic TPU Plastic Nylon Rubber Aluminum Steel Iron Titanium Steel AISI 1018 Stainless 304 Stainless 316 Aluminum 6061-T6 Aluminum 7075-T6 Brass C360 Glass Steel AISI 1045 Steel AISI 4340 Steel A992 Stainless 303 Stainless 17-4PH Aluminum 2024-T351 Aluminum 5052-H32 Aluminum 7050-T7451 Titanium Ti-6Al-4V Brass C260 Nickel Inconel 718 Magnesium AZ31B-H24 Zinc Zamak 3 Plastic ABS (bulk/injection) Plastic Polycarbonate Plastic POM/Acetal Plastic Nylon PA6 Plastic Nylon PA66 Plastic PEEK Plastic PTFE Plastic UHMWPE Plastic HDPE Plastic Polypropylene Plastic PMMA FDM ASA FDM Polycarbonate FDM PAHT-CF FDM HIPS SLA Resin Tough 2000 SLA Resin Elastic 50A SLS PA12 Nylon DMLS AlSi10Mg Aluminum DMLS Ti-6Al-4V ELI Titanium DMLS 316L Stainless Steel DMLS 17-4PH Stainless Steel Brick Copper C110 Strength against density