Thermal conductivity against densityHigher and further left: spreads more heat for its weightThermal expansion against thermal conductivityLower and further right: warps less when heated
Try it on a partA bracket to run stress or thermal on, free in your browser
Sources5 documents: Copper Development Association, Niagara LaSalle, U.S. Department of Defense, Wieland, Ovako
Copper C12200
C12200 phosphorus-deoxidized copper (DHP, the air-conditioning and refrigeration tube copper), tube annealed to 0.050 mm grain size (OS050), 0.065 in. wall, copper.org typical values
Steel AISI 1018
AISI 1018 cold drawn bar (Niagara LaSalle, cold-finished bar producer)
1
C12200 Alloy (copper.org)Copper Development Associationarchived copyCopper C12200 · Yield strength: typical, 0.5% extension under load, 0.065 in. tubeCopper C12200 · Ultimate tensile strength: typical, 0.065 in. tubeCopper C12200 · Elongation at break: typical, 0.065 in. tubeCopper C12200 · Young's modulus (stiffness): typicalCopper C12200 · Density: nominalCopper C12200 · Thermal conductivity: typical, 20 °CCopper C12200 · Thermal expansion: typical, mean 20-100 °CCopper C12200 · Specific heat: typical, 20 °CCopper C12200 · Melting point: liquidus
MIL-HDBK-5J, Metallic Materials and Elements for Aerospace Vehicle Structures (2003)U.S. Department of DefenseSteel AISI 1018 · Young's modulus (stiffness): base material: AISI 1025 plain carbon steel (MIL-HDBK-5J design value; ASTM A108 bar is the cold-finished carbon-steel bar spec that also covers 1018)Steel AISI 1018 · Density: base material: AISI 1025 plain carbon steel (MIL-HDBK-5J design value; ASTM A108 bar is the cold-finished carbon-steel bar spec that also covers 1018)Steel AISI 1018 · Poisson's ratio: base material: AISI 1025 plain carbon steel (MIL-HDBK-5J design value; ASTM A108 bar is the cold-finished carbon-steel bar spec that also covers 1018)Steel AISI 1018 · Thermal conductivity: base material: AISI 1025 plain carbon steel (MIL-HDBK-5J design value; ASTM A108 bar is the cold-finished carbon-steel bar spec that also covers 1018)Steel AISI 1018 · Specific heat: base material: AISI 1025 plain carbon steel (MIL-HDBK-5J design value; ASTM A108 bar is the cold-finished carbon-steel bar spec that also covers 1018)
4
Wieland-K19 (Cu-DHP, C12200) Data SheetWielandarchived copyCopper C12200 · Poisson's ratio: reference value at room temperature (Wieland-K19 = Cu-DHP = C12200, rolled products)
5
S275JR Steel GradeOvakoSteel AISI 1018 · Thermal expansion: base material: unalloyed carbon steel, Ovako family table (S275JR, 'none alloyed structural steels', C <= 0.21%); mean 20-300 °C
Each number points to the document that states it, with the exact basis. Values without a number are computed from the sourced ones. "Not sourced" means no citable source states it (or only a specification minimum); figures computed from it are left out too.
Questions
Mechanical
Is Copper C12200 stronger than Steel AISI 1018?
Steel AISI 1018 is stronger: its yield strength is 372 MPa against 69 MPa for Copper C12200 (5.39x).
Which is lighter, Copper C12200 or Steel AISI 1018?
Steel AISI 1018 is lighter: 7,861 kg/m³ against 8,941 kg/m³ for Copper C12200.
Which is stiffer, Copper C12200 or Steel AISI 1018?
Steel AISI 1018 is stiffer: Young's modulus 200 GPa against 117 GPa for Copper C12200, so the same part in Steel AISI 1018 deflects less under the same load.
Which is lighter for the same job, Copper C12200 or Steel AISI 1018?
For the same stiffness or strength: Steel AISI 1018 is lighter for a stiff rod or tie (tension), stiff beam (bending), stiff panel or plate, strong rod or tie, strong beam, strong panel or plate.
Part that must be
Copper C12200
Steel AISI 1018
Stiff rod or tie (tension)
1.94x heavier
lighter
Stiff beam (bending)
49% heavier
lighter
Stiff panel or plate
36% heavier
lighter
Strong rod or tie
6.13x heavier
lighter
Strong beam
3.5x heavier
lighter
Strong panel or plate
2.64x heavier
lighter
For the same stiffness or strength, mass scales with density over stiffness (or strength) raised to a power set by how the part is loaded: 1 for a rod in tension, 1/2 for a beam in bending, 1/3 for a panel (the standard material-selection indices).
Which is more ductile, Copper C12200 or Steel AISI 1018?
Copper C12200 stretches further before it breaks: 45% elongation at break against 15% for Steel AISI 1018.
Thermal
Which conducts heat better, Copper C12200 or Steel AISI 1018?
Copper C12200 conducts heat better: 339 W/m·K against 51.9 W/m·K for Steel AISI 1018.
Which expands less with temperature?
Steel AISI 1018 expands less: 12 µm/m·K against 16.9 µm/m·K for Copper C12200.