Materials / Compare

Ceramic Aluminum Nitride vs. Stainless Steel 17-4PH

Compare Ceramic Aluminum Nitride vs. Stainless Steel 17-4PH strength, stiffness, weight and thermal properties.

Change either side
Ceramic Aluminum NitrideSintered ceramic (pressed and fired)
Stainless Steel 17-4PHWrought
Try it on a partA sample part to run stress or thermal on, free in your browserOpen in LessCADOpen in LessCAD
Mechanical
Yield strengthnot sourced1,275MPasourcetypical, transverse, sheet/strip
Ultimate tensile strengthnot sourced1,379MPasourcetypical, transverse, sheet/strip
Flexural strength310MPasource3-point bending strength (JIS R 1601)not sourced
Elongation at breaknot sourced9%sourcetypical, transverse, in 2 in. (50.8 mm)
Young's modulus (stiffness)320GPasourcetypical (JIS R 1602)197GPasourceH 900
Density3,400kg/m³sourcetypical (JIS R 1634)7,800kg/m³sourceH 900
Strength to weightnot sourced163kN·m/kg
Stiffness to weight94.1MN·m/kg3.73x higher25.3MN·m/kg
Poisson's ratio0.24sourcetypical (JIS R 1602)0.272sourceH 900 (column)
Shear modulus129GPa1.67x stiffer in shear77.4GPa
Bulk modulus205GPa144GPa
Speed of sound9,701m/s5,026m/s
Thermal
Thermal conductivity150W/m·Ksourcetypical (JIS R 1611)17.9W/m·Ksourceat 149 °C (300 °F), H 900
Thermal expansion4.6µm/m·Ksourcemean, 40-400 °C (JIS R 1618)10.8µm/m·Ksourcemean, 21–93 °C (70–200 °F), H 900
100 mm part over a 50 °C swing23µm growth2.35x less54µm growth
Specific heat710J/kg·Ksourcetypical (JIS R 1611)460J/kg·Ksourcemean, 0–100 °C, H 900
Heats up and cools (diffusivity)62.1mm²/s12.5x faster4.99mm²/s
Thermal shock resistancenot sourced7,809W/m
Max service temperaturenot sourced316°Csourcestrength-retention limit (not oxidation)
Values forKYOCERA AN216A dense sintered aluminium nitride, typical values; KYOCERA Fineceramics Europe data sheet 2023.04.03Cleveland-Cliffs 17-4 PH, Condition H 900, sheet/strip, transverse (Product Data Bulletin, May 2021)

Every value links to the document that states it. "Not sourced" means no citable source states it (or only a specification minimum); figures computed from it are left out too.

Questions

Which is lighter, Ceramic Aluminum Nitride or Stainless Steel 17-4PH?

Ceramic Aluminum Nitride is lighter: 3,400 kg/m³ against 7,800 kg/m³ for Stainless Steel 17-4PH.

Which is stiffer, Ceramic Aluminum Nitride or Stainless Steel 17-4PH?

Ceramic Aluminum Nitride is stiffer: Young's modulus 320 GPa against 197 GPa for Stainless Steel 17-4PH, so the same part in Ceramic Aluminum Nitride deflects less under the same load.

Which is lighter for the same job, Ceramic Aluminum Nitride or Stainless Steel 17-4PH?

For the same stiffness or strength: Ceramic Aluminum Nitride is lighter for a stiff rod or tie (tension), stiff beam (bending), stiff panel or plate.

Part that must beCeramic Aluminum NitrideStainless Steel 17-4PH
Stiff rod or tie (tension)lighter3.73x heavier
Stiff beam (bending)lighter2.92x heavier
Stiff panel or platelighter2.7x heavier

For the same stiffness or strength, mass scales with density over stiffness (or strength) raised to a power set by how the part is loaded: 1 for a rod in tension, 1/2 for a beam in bending, 1/3 for a panel (the standard material-selection indices).

Which conducts heat better, Ceramic Aluminum Nitride or Stainless Steel 17-4PH?

Ceramic Aluminum Nitride conducts heat better: 150 W/m·K against 17.9 W/m·K for Stainless Steel 17-4PH.

Which expands less with temperature?

Ceramic Aluminum Nitride expands less: 4.6 µm/m·K against 10.8 µm/m·K for Stainless Steel 17-4PH.

Among 72 materials

1k10k0.1110100Density (kg/m³)Young's modulus (GPa)Plastic PLAPlastic PETGPlastic ABSPlastic TPUPlastic NylonAluminumSteelIronTitaniumSteel AISI 1018Stainless Steel 304Stainless Steel 316Aluminum 6061-T6Aluminum 7075-T6Brass C360Copper C110GlassSteel AISI 1045Steel AISI 4340Steel A992Stainless Steel 303Aluminum 2024-T351Aluminum 5052-H32Aluminum 7050-T7451Titanium Ti-6Al-4VBrass C260Nickel Inconel 718Magnesium AZ31B-H24Zinc Zamak 3Plastic ABS (bulk/injection)Plastic PolycarbonatePlastic POM/AcetalPlastic Nylon PA6Plastic Nylon PA66Plastic PEEKPlastic UHMWPEPlastic HDPEPlastic PolypropylenePlastic PMMAFDM ASAFDM PolycarbonateFDM PAHT-CFFDM HIPSSLA Resin Tough 2000SLS PA12 NylonDMLS AlSi10Mg AluminumDMLS Ti-6Al-4V ELI TitaniumDMLS 316L Stainless SteelDMLS 17-4PH Stainless SteelPCB Laminate FR-4SiliconCeramic Alumina 96%Aluminum A380Aluminum 6063-T6Aluminum 1100-OAluminum ADC12Magnesium AZ91DSolder SAC305Plastic PBT GF30Plastic PPS GF40Plastic LCP GF30Ceramic Aluminum NitrideStainless Steel 17-4PH
Stiffness against density
1k10k101001kDensity (kg/m³)Yield strength (MPa)Plastic PLAPlastic PETGPlastic ABSPlastic TPUPlastic NylonRubberAluminumSteelIronTitaniumSteel AISI 1018Stainless Steel 304Stainless Steel 316Aluminum 6061-T6Aluminum 7075-T6Brass C360Copper C110GlassSteel AISI 1045Steel AISI 4340Steel A992Stainless Steel 303Aluminum 2024-T351Aluminum 5052-H32Aluminum 7050-T7451Titanium Ti-6Al-4VBrass C260Nickel Inconel 718Magnesium AZ31B-H24Zinc Zamak 3Plastic ABS (bulk/injection)Plastic PolycarbonatePlastic POM/AcetalPlastic Nylon PA6Plastic Nylon PA66Plastic PEEKPlastic PTFEPlastic UHMWPEPlastic HDPEPlastic PolypropylenePlastic PMMAFDM ASAFDM PolycarbonateFDM PAHT-CFFDM HIPSSLA Resin Tough 2000SLA Resin Elastic 50ASLS PA12 NylonDMLS AlSi10Mg AluminumDMLS Ti-6Al-4V ELI TitaniumDMLS 316L Stainless SteelDMLS 17-4PH Stainless SteelBrickPCB Laminate FR-4SiliconCeramic Alumina 96%Aluminum A380Aluminum 6063-T6Aluminum 1100-OAluminum ADC12Magnesium AZ91DSolder SAC305Plastic PBT GF30Plastic PPS GF40Plastic LCP GF30Stainless Steel 17-4PH
Strength against density

Related comparisons