Materials / Compare
DMLS Ti-6Al-4V ELI Titanium vs. Drywall
Compare DMLS Ti-6Al-4V ELI Titanium vs. Drywall strength, stiffness, weight and thermal properties.
| Try it on a partA sample part to run stress or thermal on, free in your browser | Open in LessCAD | Open in LessCAD |
|---|---|---|
| Mechanical | ||
| Yield strength | 1,100MPasourcetypical, as built, average of horizontal + vertical (M400) | not given (tensile used) |
| Ultimate tensile strength | 1,270MPasourcetypical, as built, average of horizontal + vertical (M400) | 1–2MPasourceambient range reported in review (Australian studies) |
| Compressive strength | not sourced | 2.4MPasourcetypical, 70 F / 50% RH |
| Elongation at break | 8.7%sourcetypical at break, as built (M400) | not sourced |
| Young's modulus (stiffness) | 110GPasourcesame maker and process, sibling grade: EOS Titanium Ti64 (Grade 5) on EOS M 290, as built, XY and Z, typical | 1–2GPasourceambient range reported in review (Australian studies) |
| Density | 4,400kg/m³sourcetypical part density (ISO 3369), M400 | not sourced |
| Strength to weight | 250kN·m/kg | not sourced |
| Stiffness to weight | 25MN·m/kg | not sourced |
| Poisson's ratio | 0.342sourcewrought TIMETAL 6-4 (TIMET measurement, mean of 10); composition-level, not DMLS-measured | not sourced |
| Shear modulus | 41GPa | not sourced |
| Bulk modulus | 116GPa | not sourced |
| Speed of sound | 5,000m/s | not sourced |
| Thermal | ||
| Thermal conductivity | 6.6W/m·Ksourcebase material: wrought Ti-6Al-4V / 6-4 ELI (TIMET datasheet), 20 °C | not sourced |
| Thermal expansion | 9µm/m·Ksourcemean 25-100 °C, ASTM E228; EOS Ti64 Grade 23 (=ELI) on EOS M 290 40 µm; condition not stated (sheet's mechanical data are heat treated) | 16.7µm/m·Ksourcetypical, unrestrained, 3.3-32 C |
| 100 mm part over a 50 °C swing | 45µm growth1.86x less | 83.5µm growth |
| Specific heat | 580J/kg·Ksourcebase material: wrought Ti-6Al-4V / 6-4 ELI (TIMET datasheet), 20 °C | 1,090J/kg·Ksourcetypical (from ASHRAE Handbook of Fundamentals, per GA) |
| Heats up and cools (diffusivity) | 2.59mm²/s | not sourced |
| Thermal shock resistance | 4,825W/m | not sourced |
| Melting point | 1,630–1,650°Csourcemelting range, wrought TIMETAL 6-4 (composition-level) | not sourced |
| Max service temperature | not sourced | 52°Csourcemanufacturer sustained-exposure limit |
| Values for | EOS Titanium Ti64ELI (powder 9011-0040; ASTM F136/F3001, i.e. Grade 23) on EOS M400 SF, parameter set Ti64ELI_030_FlexM400_100, 30 µm, as built; ISO 6892-1 A14 | 1/2 in. (12.7 mm) regular gypsum board (ASTM C1396), Gypsum Association GA-235-2019 typical/minimum properties; tensile and E from USDA FPL-co-authored review; service limit from USG Sheetrock 1/2 in. submittal |
Every value links to the document that states it. "Not sourced" means no citable source states it (or only a specification minimum); figures computed from it are left out too.
DMLS Ti-6Al-4V ELI Titanium is 3D printed: its properties depend on build direction and print settings; these are typical values.
Questions
Is DMLS Ti-6Al-4V ELI Titanium stronger than Drywall?
DMLS Ti-6Al-4V ELI Titanium is stronger: its yield strength is 1,100 MPa against tensile strength 1.5 MPa for Drywall (733x).
Which is stiffer, DMLS Ti-6Al-4V ELI Titanium or Drywall?
DMLS Ti-6Al-4V ELI Titanium is stiffer: Young's modulus 110 GPa against 1.5 GPa for Drywall, so the same part in DMLS Ti-6Al-4V ELI Titanium deflects less under the same load.
Which expands less with temperature?
DMLS Ti-6Al-4V ELI Titanium expands less: 9 µm/m·K against 16.7 µm/m·K for Drywall.