Materials / Compare
Aluminum 7075-T6 vs. Plastic Nylon PA66
Compare Aluminum 7075-T6 vs. Plastic Nylon PA66 strength, stiffness, weight and thermal properties.
| Try it on a partA bracket to run stress or thermal on, free in your browser | Open in LessCAD | Open in LessCAD |
|---|---|---|
| Mechanical | ||
| Yield strength | 503MPasourcetypical, 0.2% offset, .500 in dia specimen | 85MPasourcetypical, dry |
| Ultimate tensile strength | 572MPasourcetypical | not sourced |
| Elongation at break | 11%sourcetypical, in 4D | 30%sourcenominal strain at break, dry |
| Young's modulus (stiffness) | 71GPasourcetypical | 3GPasourcetypical, dry |
| Density | 2,800kg/m³sourcenominal | 1,130kg/m³sourcetypical |
| Strength to weight | 180kN·m/kg2.39x higher | 75.2kN·m/kg |
| Stiffness to weight | 25.4MN·m/kg9.55x higher | 2.65MN·m/kg |
| Poisson's ratio | 0.33sourcetypical (handbook physical constant) | 0.4sourcebase material: unfilled polyamide (PA), conditioned, maker design-guide family value (Covestro Table 3-1) |
| Shear modulus | 26.7GPa24.9x stiffer in shear | 1.07GPa |
| Bulk modulus | 69.6GPa | 5GPa |
| Speed of sound | 5,036m/s | 1,629m/s |
| Thermal | ||
| Thermal conductivity | 130W/m·Ksourcetypical, 20 °C, T651 | 0.33W/m·Ksourcetypical |
| Thermal expansion | 23.4µm/m·Ksourcetypical, mean 20-100 °C | 98µm/m·Ksourcelongitudinal, 23-55 °C |
| 100 mm part over a 50 °C swing | 117µm growth4.19x less | 490µm growth |
| Specific heat | 960J/kg·Ksourcetypical, at 100 °C | 1,700J/kg·Ksourcetypical |
| Heats up and cools (diffusivity) | 48.4mm²/s282x faster | 0.172mm²/s |
| Thermal shock resistance | 26,370W/m461x more resistant | 57.2W/m |
| Melting point | 532–635°Csourcemelting range | 260°CsourceDSC |
| Max service temperature | not sourced | 101°CsourceIEC 60216 temperature index, 20000 h |
| Values for | 7075-T6/T651, Kaiser Aluminum rod & bar (mechanical) and sheet/coil/plate (physical) typical datasheets; Poisson from MIL-HDBK-5J | BASF Ultramid A3K (PA66, unreinforced injection-moulding grade), Product Information 02/2026, dry values (ISO methods) |
Every value links to the document that states it. "Not sourced" means no citable source states it (or only a specification minimum); figures computed from it are left out too.
Questions
Is Aluminum 7075-T6 stronger than Plastic Nylon PA66?
Aluminum 7075-T6 is stronger: its yield strength is 503 MPa against 85 MPa for Plastic Nylon PA66 (5.92x).
Which is lighter, Aluminum 7075-T6 or Plastic Nylon PA66?
Plastic Nylon PA66 is lighter: 1,130 kg/m³ against 2,800 kg/m³ for Aluminum 7075-T6.
Which is stiffer, Aluminum 7075-T6 or Plastic Nylon PA66?
Aluminum 7075-T6 is stiffer: Young's modulus 71 GPa against 3 GPa for Plastic Nylon PA66, so the same part in Aluminum 7075-T6 deflects less under the same load.
Which is lighter for the same job, Aluminum 7075-T6 or Plastic Nylon PA66?
For the same stiffness or strength: Aluminum 7075-T6 is lighter for a stiff rod or tie (tension), stiff beam (bending), stiff panel or plate, strong rod or tie, strong beam; Plastic Nylon PA66 is lighter for a strong panel or plate.
| Part that must be | Aluminum 7075-T6 | Plastic Nylon PA66 |
|---|---|---|
| Stiff rod or tie (tension) | lighter | 9.55x heavier |
| Stiff beam (bending) | lighter | 1.96x heavier |
| Stiff panel or plate | lighter | 16% heavier |
| Strong rod or tie | lighter | 2.39x heavier |
| Strong beam | lighter | 32% heavier |
| Strong panel or plate | 2% heavier | lighter |
For the same stiffness or strength, mass scales with density over stiffness (or strength) raised to a power set by how the part is loaded: 1 for a rod in tension, 1/2 for a beam in bending, 1/3 for a panel (the standard material-selection indices).
Which conducts heat better, Aluminum 7075-T6 or Plastic Nylon PA66?
Aluminum 7075-T6 conducts heat better: 130 W/m·K against 0.33 W/m·K for Plastic Nylon PA66.
Which expands less with temperature?
Aluminum 7075-T6 expands less: 23.4 µm/m·K against 98 µm/m·K for Plastic Nylon PA66.