Aluminum 2024-T351 vs. Plastic ABS (bulk/injection)

Compare Aluminum 2024-T351 vs. Plastic ABS (bulk/injection) strength, stiffness, weight and thermal properties.

Change either side

Aluminum 2024-T351Wrought

Plastic ABS (bulk/injection)Bulk polymer (molded or machined)

Mechanical
Try it on a partA bracket to run stress or thermal on, free in your browser	Open in LessCAD	Open in LessCAD
Yield strength	324MPasourcetypical, 0.2% offset, .500 in dia specimen	45MPasourcetypical, tensile stress at yield 23 °C
Ultimate tensile strength	469MPasourcetypical	not sourced
Flexural strength	not sourced	65MPasourcetypical, 23 °C
Elongation at break	19%sourcetypical, in 4D	10%sourcenominal strain at break, 23 °C
Young's modulus (stiffness)	73.1GPasourcetypical31.8x stiffer	2.3GPasourcetypical
Density	2,770kg/m³sourcenominal	1,040kg/m³sourcetypical
Strength to weight	117kN·m/kg2.7x higher	43.3kN·m/kg
Stiffness to weight	26.4MN·m/kg11.9x higher	2.21MN·m/kg
Poisson's ratio	0.33sourcetypical (handbook physical constant), all tempers	0.39sourcetypical, ABS family (Covestro Part and Mold Design guide, Table 3-1)
Shear modulus	27.5GPa33.2x stiffer in shear	0.827GPa
Bulk modulus	71.7GPa	3.48GPa
Speed of sound	5,137m/s	1,487m/s
Thermal
Thermal conductivity	120W/m·Ksourcetypical, 20 °C	0.17W/m·Ksourcetypical
Thermal expansion	22.9µm/m·Ksourcetypical, mean 20-100 °C	80–110µm/m·Ksourcerange
100 mm part over a 50 °C swing	115µm growth4.15x less	475µm growth
Specific heat	875J/kg·Ksourcetypical, at 100 °C	not sourced
Heats up and cools (diffusivity)	49.5mm²/s	not sourced
Thermal shock resistance	15,561W/m729x more resistant	21.4W/m
Melting point	502–638°Csourcemelting range	not sourced
Max service temperature	not sourced	94°CsourceHDT 1.8 MPa (annealed 4 h/80 °C)
Values for	2024-T4/T351, Kaiser Aluminum sheet, coil & plate typical datasheet; Poisson from MIL-HDBK-5J	INEOS Styrolution Terluran GP-22 general-purpose injection-molding ABS, ISO typical values (TDS revision 08/01/2022)

Every value links to the document that states it. "Not sourced" means no citable source states it (or only a specification minimum); figures computed from it are left out too.

Questions

Is Aluminum 2024-T351 stronger than Plastic ABS (bulk/injection)?

Aluminum 2024-T351 is stronger: its yield strength is 324 MPa against 45 MPa for Plastic ABS (bulk/injection) (7.2x).

Which is lighter, Aluminum 2024-T351 or Plastic ABS (bulk/injection)?

Plastic ABS (bulk/injection) is lighter: 1,040 kg/m³ against 2,770 kg/m³ for Aluminum 2024-T351.

Which is stiffer, Aluminum 2024-T351 or Plastic ABS (bulk/injection)?

Aluminum 2024-T351 is stiffer: Young's modulus 73.1 GPa against 2.3 GPa for Plastic ABS (bulk/injection), so the same part in Aluminum 2024-T351 deflects less under the same load.

Which is lighter for the same job, Aluminum 2024-T351 or Plastic ABS (bulk/injection)?

For the same stiffness or strength: Aluminum 2024-T351 is lighter for a stiff rod or tie (tension), stiff beam (bending), stiff panel or plate, strong rod or tie, strong beam.

Part that must be	Aluminum 2024-T351	Plastic ABS (bulk/injection)
Stiff rod or tie (tension)	lighter	11.9x heavier
Stiff beam (bending)	lighter	2.12x heavier
Stiff panel or plate	lighter	19% heavier
Strong rod or tie	lighter	2.7x heavier
Strong beam	lighter	40% heavier
Strong panel or plate	about equal	about equal

For the same stiffness or strength, mass scales with density over stiffness (or strength) raised to a power set by how the part is loaded: 1 for a rod in tension, 1/2 for a beam in bending, 1/3 for a panel (the standard material-selection indices).

Which conducts heat better, Aluminum 2024-T351 or Plastic ABS (bulk/injection)?

Aluminum 2024-T351 conducts heat better: 120 W/m·K against 0.17 W/m·K for Plastic ABS (bulk/injection).

Which expands less with temperature?

Aluminum 2024-T351 expands less: 22.9 µm/m·K against 95 µm/m·K for Plastic ABS (bulk/injection).