Aluminum 6063-T6 vs. DMLS Ti-6Al-4V ELI Titanium

Compare Aluminum 6063-T6 vs. DMLS Ti-6Al-4V ELI Titanium strength, stiffness, weight and thermal properties.

Change either side

DMLS Ti-6Al-4V ELI Titanium3D printed metal (DMLS)

Mechanical
Try it on a partA bracket to run stress or thermal on, free in your browser	Open in LessCAD	Open in LessCAD
Yield strength	215MPasourcetypical, T6, 0.0625 in specimen	1,100MPasourcetypical, as built, average of horizontal + vertical (M400)
Ultimate tensile strength	240MPasourcetypical, T6	1,270MPasourcetypical, as built, average of horizontal + vertical (M400)
Elongation at break	12%sourcetypical, T6, in 4D	8.7%sourcetypical at break, as built (M400)
Young's modulus (stiffness)	69GPasourcetypical	110GPasourcesame maker and process, sibling grade: EOS Titanium Ti64 (Grade 5) on EOS M 290, as built, XY and Z, typical
Density	2,700kg/m³sourcenominal, 20 °C	4,400kg/m³sourcetypical part density (ISO 3369), M400
Strength to weight	79.6kN·m/kg	250kN·m/kg3.14x higher
Stiffness to weight	25.6MN·m/kg2% higher	25MN·m/kg
Poisson's ratio	not sourced	0.342sourcewrought TIMETAL 6-4 (TIMET measurement, mean of 10); composition-level, not DMLS-measured
Shear modulus	not sourced	41GPa
Bulk modulus	not sourced	116GPa
Speed of sound	5,055m/s	5,000m/s
Thermal
Thermal conductivity	201W/m·Ksourcetypical, T6, 20 °C	6.6W/m·Ksourcebase material: wrought Ti-6Al-4V / 6-4 ELI (TIMET datasheet), 20 °C
Thermal expansion	23.4µm/m·Ksourcetypical, mean 20-100 °C	9µm/m·Ksourcemean 25-100 °C, ASTM E228; EOS Ti64 Grade 23 (=ELI) on EOS M 290 40 µm; condition not stated (sheet's mechanical data are heat treated)
100 mm part over a 50 °C swing	117µm growth	45µm growth2.6x less
Specific heat	901J/kg·Ksourcetypical, 20 °C (Hydro EN AW-6063)	580J/kg·Ksourcebase material: wrought Ti-6Al-4V / 6-4 ELI (TIMET datasheet), 20 °C
Heats up and cools (diffusivity)	82.6mm²/s31.9x faster	2.59mm²/s
Thermal shock resistance	not sourced	4,825W/m
Melting point	615–655°Csourcemelting range	1,630–1,650°Csourcemelting range, wrought TIMETAL 6-4 (composition-level)
Values for	6063-T6 extruded tube, Kaiser Aluminum Tube & Pipe Alloy 6063 Technical Data (Rev. 05/06), typical properties; specific heat from Hydro EN AW-6063 extruded-products datasheet (Rev.4, 03/2023).	EOS Titanium Ti64ELI (powder 9011-0040; ASTM F136/F3001, i.e. Grade 23) on EOS M400 SF, parameter set Ti64ELI_030_FlexM400_100, 30 µm, as built; ISO 6892-1 A14

Every value links to the document that states it. "Not sourced" means no citable source states it (or only a specification minimum); figures computed from it are left out too.

DMLS Ti-6Al-4V ELI Titanium is 3D printed: its properties depend on build direction and print settings; these are typical values.

Questions

Is Aluminum 6063-T6 stronger than DMLS Ti-6Al-4V ELI Titanium?

DMLS Ti-6Al-4V ELI Titanium is stronger: its yield strength is 1,100 MPa against 215 MPa for Aluminum 6063-T6 (5.12x).

Which is lighter, Aluminum 6063-T6 or DMLS Ti-6Al-4V ELI Titanium?

Aluminum 6063-T6 is lighter: 2,700 kg/m³ against 4,400 kg/m³ for DMLS Ti-6Al-4V ELI Titanium.

Which is stiffer, Aluminum 6063-T6 or DMLS Ti-6Al-4V ELI Titanium?

DMLS Ti-6Al-4V ELI Titanium is stiffer: Young's modulus 110 GPa against 69 GPa for Aluminum 6063-T6, so the same part in DMLS Ti-6Al-4V ELI Titanium deflects less under the same load.

Which is lighter for the same job, Aluminum 6063-T6 or DMLS Ti-6Al-4V ELI Titanium?

For the same stiffness or strength: Aluminum 6063-T6 is lighter for a stiff rod or tie (tension), stiff beam (bending), stiff panel or plate; DMLS Ti-6Al-4V ELI Titanium is lighter for a strong rod or tie, strong beam, strong panel or plate.

Part that must be	Aluminum 6063-T6	DMLS Ti-6Al-4V ELI Titanium
Stiff rod or tie (tension)	lighter	2% heavier
Stiff beam (bending)	lighter	29% heavier
Stiff panel or plate	lighter	40% heavier
Strong rod or tie	3.14x heavier	lighter
Strong beam	1.82x heavier	lighter
Strong panel or plate	39% heavier	lighter

For the same stiffness or strength, mass scales with density over stiffness (or strength) raised to a power set by how the part is loaded: 1 for a rod in tension, 1/2 for a beam in bending, 1/3 for a panel (the standard material-selection indices).

Which conducts heat better, Aluminum 6063-T6 or DMLS Ti-6Al-4V ELI Titanium?

Aluminum 6063-T6 conducts heat better: 201 W/m·K against 6.6 W/m·K for DMLS Ti-6Al-4V ELI Titanium.

Which expands less with temperature?

DMLS Ti-6Al-4V ELI Titanium expands less: 9 µm/m·K against 23.4 µm/m·K for Aluminum 6063-T6.

Among 72 materials

Stiffness against density

Strength against density