Materials / Compare
Brass C360 vs. FDM ASA
Compare Brass C360 vs. FDM ASA strength, stiffness, weight and thermal properties.
| Try it on a partA bracket to run stress or thermal on, free in your browser | Open in LessCAD | Open in LessCAD |
|---|---|---|
| Mechanical | ||
| Yield strength | 310MPasourcetypical, 0.5% extension under load | not given (tensile used) |
| Ultimate tensile strength | 400MPasourcetypical10.8x stronger | 37MPasourcetypical |
| Flexural strength | not sourced | 65MPasourcetypical |
| Elongation at break | 25%sourcetypical, 1 in. rod | 9.2%sourcetypical |
| Young's modulus (stiffness) | 96.5GPasourcetypical, temper-independent | 2.45GPasourcetypical |
| Density | 8,498kg/m³sourcenominal | 1,050kg/m³sourcetypical |
| Strength to weight | 36.5kN·m/kg4% higher | 35.2kN·m/kg |
| Stiffness to weight | 11.4MN·m/kg4.87x higher | 2.33MN·m/kg |
| Poisson's ratio | 0.34sourcebase material: leaded free-machining brass CuZn39Pb2 (C37700), Wieland-Z30 rolled products, reference value at room temperature | not sourced |
| Shear modulus | 36GPa | not sourced |
| Bulk modulus | 101GPa | not sourced |
| Speed of sound | 3,370m/s | 1,528m/s |
| Thermal | ||
| Thermal conductivity | 116W/m·Ksourcetypical, 20 °C | 0.17W/m·Ksourcebase material: INEOS Styrolution Luran S 777K injection-molding ASA, typical |
| Thermal expansion | 20.5µm/m·Ksourcetypical, mean 20-300 °C | 80–110µm/m·Ksourcebase material: INEOS Styrolution Luran S 777K injection-molding ASA, range |
| 100 mm part over a 50 °C swing | 103µm growth4.63x less | 475µm growth |
| Specific heat | 377J/kg·Ksourcetypical, 20 °C | not sourced |
| Heats up and cools (diffusivity) | 36.2mm²/s | not sourced |
| Thermal shock resistance | 11,997W/m | not sourced |
| Melting point | 888–899°Csourcesolidus-liquidus | not sourced |
| Max service temperature | not sourced | 92°CsourceHDT 1.8 MPa |
| Values for | C36000 free-cutting brass, H02 half-hard rod 1 in. section (20% cold work), copper.org typical values | Bambu Lab ASA, TDS V3.0, printed specimens X-Y; nozzle 260 °C, bed 80 °C, 200 mm/s, 100% infill; annealed and dried 80 °C for 12 h before testing. |
Every value links to the document that states it. "Not sourced" means no citable source states it (or only a specification minimum); figures computed from it are left out too.
FDM ASA is 3D printed: its properties depend on build direction and print settings; these are typical values.
Questions
Is Brass C360 stronger than FDM ASA?
Brass C360 is stronger: its yield strength is 310 MPa against tensile strength 37 MPa for FDM ASA (8.38x).
Which is lighter, Brass C360 or FDM ASA?
FDM ASA is lighter: 1,050 kg/m³ against 8,498 kg/m³ for Brass C360.
Which is stiffer, Brass C360 or FDM ASA?
Brass C360 is stiffer: Young's modulus 96.5 GPa against 2.45 GPa for FDM ASA, so the same part in Brass C360 deflects less under the same load.
Which is lighter for the same job, Brass C360 or FDM ASA?
For the same stiffness or strength: Brass C360 is lighter for a stiff rod or tie (tension), strong rod or tie; FDM ASA is lighter for a stiff beam (bending), stiff panel or plate, strong beam, strong panel or plate.
| Part that must be | Brass C360 | FDM ASA |
|---|---|---|
| Stiff rod or tie (tension) | lighter | 4.87x heavier |
| Stiff beam (bending) | 29% heavier | lighter |
| Stiff panel or plate | 2.38x heavier | lighter |
| Strong rod or tie | lighter | 4% heavier |
| Strong beam | 1.96x heavier | lighter |
| Strong panel or plate | 2.8x heavier | lighter |
For the same stiffness or strength, mass scales with density over stiffness (or strength) raised to a power set by how the part is loaded: 1 for a rod in tension, 1/2 for a beam in bending, 1/3 for a panel (the standard material-selection indices).
Which conducts heat better, Brass C360 or FDM ASA?
Brass C360 conducts heat better: 116 W/m·K against 0.17 W/m·K for FDM ASA.
Which expands less with temperature?
Brass C360 expands less: 20.5 µm/m·K against 95 µm/m·K for FDM ASA.