Aluminum 7050-T7451 vs. Aluminum ADC12

Compare Aluminum 7050-T7451 vs. Aluminum ADC12 strength, stiffness, weight and thermal properties.

Change either side

Mechanical
Try it on a partA bracket to run stress or thermal on, free in your browser	Open in LessCAD	Open in LessCAD
Yield strength	469MPasourcetypical, longitudinal, 0.2% offset	149MPasourceone test result, 0.2% proof stress, as cast, ASTM tensile bar (Daiki)
Ultimate tensile strength	524MPasourcetypical, longitudinal	345MPasourceone test result, as cast, ASTM tensile bar (Daiki)
Elongation at break	11%sourcetypical, longitudinal	2.3%sourceone test result, as cast, ASTM tensile bar (Daiki)
Young's modulus (stiffness)	70.3GPasourcetypical	79.8GPasourcestandard value (S.S.Aluminum)
Density	2,830kg/m³sourcenominal	2,680kg/m³sourcemeasured (Daiki)
Strength to weight	166kN·m/kg2.98x higher	55.6kN·m/kg
Stiffness to weight	24.8MN·m/kg	29.8MN·m/kg20% higher
Poisson's ratio	0.33sourcetypical (handbook physical constant)	not sourced
Shear modulus	26.4GPa	not sourced
Bulk modulus	68.9GPa	not sourced
Speed of sound	4,984m/s	5,457m/s
Thermal
Thermal conductivity	157W/m·Ksourcetypical, 20 °C	125W/m·Ksourcemeasured on specimens cut from a 50 x 100 x 5 mm flat die casting (Daiki)
Thermal expansion	23.5µm/m·Ksourcetypical, mean 20-100 °C	21µm/m·Ksourcemeasured, temperature range not stated (Daiki)
100 mm part over a 50 °C swing	118µm growth	105µm growth12% less
Specific heat	860J/kg·Ksourcetypical, at 100 °C	911J/kg·Ksourcemeasured (Daiki)
Heats up and cools (diffusivity)	64.5mm²/s26% faster	51.2mm²/s
Thermal shock resistance	29,862W/m	not sourced
Melting point	524–635°Csourcemelting range	515–582°Csourcesolidus-liquidus (Daiki)
Values for	7050-T7451 plate, Kaiser Aluminum sheet, coil & plate typical datasheet (longitudinal); Poisson from MIL-HDBK-5J	JIS ADC12 (Al-Si-Cu, about A383 / EN AC-46100) high-pressure die-casting alloy, as cast; physical properties from Daiki Aluminium Industry (ADC12 ingot producer) measured values; modulus from S.S.Aluminum (ADC12 ingot producer) standard values.

Every value links to the document that states it. "Not sourced" means no citable source states it (or only a specification minimum); figures computed from it are left out too.

Questions

Is Aluminum 7050-T7451 stronger than Aluminum ADC12?

Aluminum 7050-T7451 is stronger: its yield strength is 469 MPa against 149 MPa for Aluminum ADC12 (3.15x).

Which is lighter, Aluminum 7050-T7451 or Aluminum ADC12?

Aluminum ADC12 is lighter: 2,680 kg/m³ against 2,830 kg/m³ for Aluminum 7050-T7451.

Which is stiffer, Aluminum 7050-T7451 or Aluminum ADC12?

Aluminum ADC12 is stiffer: Young's modulus 79.8 GPa against 70.3 GPa for Aluminum 7050-T7451, so the same part in Aluminum ADC12 deflects less under the same load.

Which is lighter for the same job, Aluminum 7050-T7451 or Aluminum ADC12?

For the same stiffness or strength: Aluminum 7050-T7451 is lighter for a strong rod or tie, strong beam, strong panel or plate; Aluminum ADC12 is lighter for a stiff rod or tie (tension), stiff beam (bending), stiff panel or plate.

Part that must be	Aluminum 7050-T7451	Aluminum ADC12
Stiff rod or tie (tension)	20% heavier	lighter
Stiff beam (bending)	13% heavier	lighter
Stiff panel or plate	10% heavier	lighter
Strong rod or tie	lighter	2.98x heavier
Strong beam	lighter	2.03x heavier
Strong panel or plate	lighter	1.68x heavier

For the same stiffness or strength, mass scales with density over stiffness (or strength) raised to a power set by how the part is loaded: 1 for a rod in tension, 1/2 for a beam in bending, 1/3 for a panel (the standard material-selection indices).

Which conducts heat better, Aluminum 7050-T7451 or Aluminum ADC12?

Aluminum 7050-T7451 conducts heat better: 157 W/m·K against 125 W/m·K for Aluminum ADC12.

Which expands less with temperature?

Aluminum ADC12 expands less: 21 µm/m·K against 23.5 µm/m·K for Aluminum 7050-T7451.

Among 72 materials

Stiffness against density

Strength against density