Aluminum 7050-T7451 vs. Plastic ABS (bulk/injection)

Compare Aluminum 7050-T7451 vs. Plastic ABS (bulk/injection) strength, stiffness, weight and thermal properties.

Change either side

Plastic ABS (bulk/injection)Bulk polymer (molded or machined)

Mechanical
Try it on a partA bracket to run stress or thermal on, free in your browser	Open in LessCAD	Open in LessCAD
Yield strength	469MPasourcetypical, longitudinal, 0.2% offset	45MPasourcetypical, tensile stress at yield 23 °C
Ultimate tensile strength	524MPasourcetypical, longitudinal	not sourced
Flexural strength	not sourced	65MPasourcetypical, 23 °C
Elongation at break	11%sourcetypical, longitudinal	10%sourcenominal strain at break, 23 °C
Young's modulus (stiffness)	70.3GPasourcetypical30.6x stiffer	2.3GPasourcetypical
Density	2,830kg/m³sourcenominal	1,040kg/m³sourcetypical
Strength to weight	166kN·m/kg3.83x higher	43.3kN·m/kg
Stiffness to weight	24.8MN·m/kg11.2x higher	2.21MN·m/kg
Poisson's ratio	0.33sourcetypical (handbook physical constant)	0.39sourcetypical, ABS family (Covestro Part and Mold Design guide, Table 3-1)
Shear modulus	26.4GPa31.9x stiffer in shear	0.827GPa
Bulk modulus	68.9GPa	3.48GPa
Speed of sound	4,984m/s	1,487m/s
Thermal
Thermal conductivity	157W/m·Ksourcetypical, 20 °C	0.17W/m·Ksourcetypical
Thermal expansion	23.5µm/m·Ksourcetypical, mean 20-100 °C	80–110µm/m·Ksourcerange
100 mm part over a 50 °C swing	118µm growth4.04x less	475µm growth
Specific heat	860J/kg·Ksourcetypical, at 100 °C	not sourced
Heats up and cools (diffusivity)	64.5mm²/s	not sourced
Thermal shock resistance	29,862W/m1,398x more resistant	21.4W/m
Melting point	524–635°Csourcemelting range	not sourced
Max service temperature	not sourced	94°CsourceHDT 1.8 MPa (annealed 4 h/80 °C)
Values for	7050-T7451 plate, Kaiser Aluminum sheet, coil & plate typical datasheet (longitudinal); Poisson from MIL-HDBK-5J	INEOS Styrolution Terluran GP-22 general-purpose injection-molding ABS, ISO typical values (TDS revision 08/01/2022)

Every value links to the document that states it. "Not sourced" means no citable source states it (or only a specification minimum); figures computed from it are left out too.

Questions

Is Aluminum 7050-T7451 stronger than Plastic ABS (bulk/injection)?

Aluminum 7050-T7451 is stronger: its yield strength is 469 MPa against 45 MPa for Plastic ABS (bulk/injection) (10.4x).

Which is lighter, Aluminum 7050-T7451 or Plastic ABS (bulk/injection)?

Plastic ABS (bulk/injection) is lighter: 1,040 kg/m³ against 2,830 kg/m³ for Aluminum 7050-T7451.

Which is stiffer, Aluminum 7050-T7451 or Plastic ABS (bulk/injection)?

Aluminum 7050-T7451 is stiffer: Young's modulus 70.3 GPa against 2.3 GPa for Plastic ABS (bulk/injection), so the same part in Aluminum 7050-T7451 deflects less under the same load.

Which is lighter for the same job, Aluminum 7050-T7451 or Plastic ABS (bulk/injection)?

For the same stiffness or strength: Aluminum 7050-T7451 is lighter for a stiff rod or tie (tension), stiff beam (bending), stiff panel or plate, strong rod or tie, strong beam, strong panel or plate.

Part that must be	Aluminum 7050-T7451	Plastic ABS (bulk/injection)
Stiff rod or tie (tension)	lighter	11.2x heavier
Stiff beam (bending)	lighter	2.03x heavier
Stiff panel or plate	lighter	15% heavier
Strong rod or tie	lighter	3.83x heavier
Strong beam	lighter	1.75x heavier
Strong panel or plate	lighter	19% heavier

For the same stiffness or strength, mass scales with density over stiffness (or strength) raised to a power set by how the part is loaded: 1 for a rod in tension, 1/2 for a beam in bending, 1/3 for a panel (the standard material-selection indices).

Which conducts heat better, Aluminum 7050-T7451 or Plastic ABS (bulk/injection)?

Aluminum 7050-T7451 conducts heat better: 157 W/m·K against 0.17 W/m·K for Plastic ABS (bulk/injection).

Which expands less with temperature?

Aluminum 7050-T7451 expands less: 23.5 µm/m·K against 95 µm/m·K for Plastic ABS (bulk/injection).

Among 59 materials

Stiffness against density

Strength against density